1.1730 is medium carbon unalloyed tool steel grade offering reasonable tensile strength. This grade can be hardened and tempered to produce a good surface hardness with moderate wear resistance. 1.1730 is widely used for components that require good machinability and wear resistant properties but does not justify the costs of an alloyed tool steel. Available from stock as cut plate.

Mechanical Properties

In normalized condition, +N

Thickness (mm) <16 16 < t <100 100 < t < 250
Yield Strength Rp0,2 [N/mm2] min. 340 min. 305 min. 275
Tensile Strengtht Rm [N/mm2] min. 620 min. 580 min. 560
Elongation A5 [%] min. 14 min. 16 min. 16
Chemical Composition
Steel C Si Mn Cr Mo S Others
C45 0,42%
<0,40% 0,50%
<0,40% 0,22% <0,035% (Pb>